Dry Sliding Tribological Behavior Of Az31 Magnesium Alloy Irradiated By High-intensity Pulsed Ion Beam

E-Book Overview

Elseiver. Applied Surface Science 257 (2010) 72–81 The dry sliding tribological behavior of AZ31 magnesium alloy irradiated by high-intensity pulsed ion beam (HIPIB) at energy density of 3.4 J/cm2 with 10 shots is investigated by dry sliding wear tests in order to explore the effect of HIPIB irradiation on tribological property of magnesium alloy. Surface morphologies, composition and structure of the irradiated AZ31 magnesium alloys are examined by electron probe microanalysis (EPMA) and X-ray diffraction (XRD). The results indicated that HIPIB irradiation led to the increase in surface microhardness and the reduction in friction coefficient and wear rate. Wear rate for both the original and the irradiated samples increased with increasing sliding load from 0.1 to 0.5N. The transition from severe metallic wear to mild oxidative wear induced by HIPIB irradiation was observed by a combined analysis in surface morphology and chemical composition of wear tracks, mechanically mixed materials and wear debris, which is mainly attributed to the significant increase in microhardness resulting from grain refinement on the irradiated surface. In addition, defects induced by HIPIB irradiation promoted the diffusion of oxygen during sliding wear and therefore led to the formation of compact mixed materials and protective films on the wear tracks surface, which also contributes to the transition in wear mechanism of AZ31 magnesium alloy induced by HIPIB irradiation.

E-Book Content

Applied Surface Science 257 (2010) 72–81 Contents lists available at ScienceDirect Applied Surface Science journal homepage: www.elsevier.com/locate/apsusc Dry sliding tribological behavior of AZ31 magnesium alloy irradiated by high-intensity pulsed ion beam P. Li a,b,∗ , M.K. Lei b,∗∗ , X.P. Zhu b a b Department of Physics and Information Engineering, Shangqiu Normal University, Shangqiu 476000, China Surface Engineering Laboratory, School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China a r t i c l e i n f o Article history: Received 19 February 2010 Received in revised form 8 June 2010 Accepted 12 June 2010 Available online 22 June 2010 PACS: 81.65.−b 81.40.Pq Keywords: Magnesium alloy High-intensity pulsed ion beam Dry sliding tribology Friction coefficient Wear mechanism a b s t r a c t The dry sliding tribological behavior of AZ31 magnesium alloy irradiated by high-intensity pulsed ion beam (HIPIB) at energy density of 3.4 J/cm2 with 10 shots is investigated by dry sliding wear tests in order to explore the effect of HIPIB irradiation on tribological property of magnesium alloy. Surface morphologies, composition and structure of the irradiated AZ31 magnesium alloys are examined by electron probe microanalysis (EPMA) and X-ray diffraction (XRD). The results indicated that HIPIB irradiation led to the increase in surface microhardness and the reduction in friction coefficient and wear rate. Wear rate for both the original and the irradiated samples increased with increasing sliding load from 0.1 to 0.5 N. The transition from severe metallic wear to mild oxidative wear induced by HIPIB irradiation was observed by a combined analysis in surface morphology and chemical composition of wear tracks, mechanically mixed materials and wear debris, which is mainly attributed to the significant increase in microhardness resulting from grain refinement on the irradiated surface. In addition, defects induced by HIPIB irradiation promoted the diffusion of oxygen during sliding wear and therefore led to the formation of compact mixed materials and protective films on the wear tracks surface, which also contributes to the transition in wear mechanism of AZ31 magnesium alloy induced by HIPIB irradiation. © 2010 Elsevier B.V. All rights reserved. 1. Introductio
You might also like

Mechanical Engineer's Data Handbook
Authors: James Carvill    208    0


Mechanics Of Sheet Metal Forming
Authors: Jack Hu , Zdzislaw Marciniak , John Duncan    191    0


Welding Operations Ii
Authors: U.S. Army and www.survivalebooks.com    134    0




Kinematic Geometry Of Surface Machining
Authors: Stephen P. Radzevich    130    0


123 Robotics Experiments For The Evil Genius
Authors: Myke Predko    128    0


основы материаловедения
Authors: Чумаченко Ю.Т.    141    0


Reliability And Optimal Maintenance
Authors: Hongzhou Wang , H. Pham    104    0


Fatigue Testing And Analysis. Theory And Practice
Authors: Yung-Li Lee , Jwo Pan , Richard Hathaway , Mark Barkey    146    0