Dynamic Response Of Metals Under High-intensity Pulsed Ion Beam Irradiation For Surface Modification

E-Book Overview

Elseiver. Nuclear Instruments and Metods in Physics Research B Volume 272, 1 February 2012, pp. 454-457
A piezoelectric transducer based on lead–zirconte–titanate (PZT) piezoelectric ceramic thin plate was appliedtocharacterize thestress waves intitaniumtargets under high-intensitypulsed ionbeam (HIPIB) irradiation at a peak accelerating voltage of 350 kV and an ion current density up to 400 A/cm2 with pulse duration of about 150ns. The magnitude of recorded stress wave signals was increased along with the irradiation intensity, presenting a slow growth with a value below 100 V in the range of 200–300 A/cm2 , and then a rapid increase of about four times up to 400 A/cm2 . The measured stress waves were explained by space–time diagram analysis. The generation and propagation of the stress wave can be attributed to the coupled thermal–dynamic effects during HIPIB irradiation onto metallic targets, where the thermal shock due to ultra-fast heating/cooling process and there coil impulse due to ablation process have a combined contribution to the induced stress waves, dependent on the irradiation intensity. It is indicated that a fast attenuation of stress wave proceeded during its propagation from the irradiated surface to the target/PZT interface. The large amount of energy delivered by the stress wave effectively converted and dissipated into plastic deformation and/or defects formation in target materials. The dynamic response of metallic materials under HIPIB irradiation accounts for the effective surface modification of metals and alloys into a depth well beyond the ion range.

E-Book Content

Nuclear Instruments and Methods in Physics Research B xxx (2011) xxx–xxx Contents lists available at ScienceDirect Nuclear Instruments and Methods in Physics Research B journal homepage: www.elsevier.com/locate/nimb Dynamic response of metals under high-intensity pulsed ion beam irradiation for surface modification X.P. Zhu, F.G. Zhang, Y. Tang, J.P. Xin, M.K. Lei ⇑ Surface Engineering Laboratory, School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China a r t i c l e i n f o Article history: Available online xxxx Keywords: High-intensity pulsed ion beam Stress wave Thermal–dynamic effect Surface modification Titanium a b s t r a c t A piezoelectric transducer based on lead–zirconte–titanate (PZT) piezoelectric ceramic thin plate was applied to characterize the stress waves in titanium targets under high-intensity pulsed ion beam (HIPIB) irradiation at a peak accelerating voltage of 350 kV and an ion current density up to 400 A/cm2 with pulse duration of about 150 ns. The magnitude of recorded stress wave signals was increased along with the irradiation intensity, presenting a slow growth with a value below 100 V in the range of 200–300 A/cm2, and then a rapid increase of about four times up to 400 A/cm2. The measured stress waves were explained by space–time diagram analysis. The generation and propagation of the stress wave can be attributed to the coupled thermal–dynamic effects during HIPIB irradiation onto metallic targets, where the thermal shock due to ultra-fast heating/cooling process and the recoil impulse due to ablation process have a combined contribution to the induced stress waves, dependent on the irradiation intensity. It is indicated that a fast attenuation of stress wave proceeded during its propagation from the irradiated surface to the target/PZT interface. The large amount of energy delivered by the stress wave effectively converted and dissipated into plastic deformation and/or defects formation in target materials. The dynamic response of metallic materials under HIPIB irradiation accounts for the effective surface modification of metals and alloys into a depth well beyond the ion range. Ó 2011
You might also like

плазменное упрочнение и напыление
Authors: Лащенко Г.И.    233    0


краткий справочник машиностроителя
Authors: Близнянский А.С. и др.    170    0


Hydrodynamics Of Pumps
Authors: Christopher E. Brennen    154    0


Concise Encyclopedia Of The Structure Of Materials
Authors: J. W. Martin Emeritus Reader in Physical Metallurgy    126    0


Materials Engineering. Science, Processing And Design
Authors: MichaelAshby    134    0



организация производства. уч. пос
Authors: Серебренников Г.Г.    152    0


основы материаловедения
Authors: Чумаченко Ю.Т.    144    0


курсовое и дипломное проектирование
Authors: Беляев П.С. , и др.    166    0


технология машиностроения (учебное пособие)
Authors: Муратов В.И. , и др.    154    0