E-Book Overview
Статья. Опубликована в журнале "Maintenance and reliability". – 2010. – Vol. 2010 – P. 61-71.
Авторы: Edward Wantuch, Bogusław Rajchel, Tadeusz Burakowski, Jacek Rońda.Статья на польском и английском языках.Название на русском языке: Влияние магнитного поля во время магнитно-абразивного полирования от выбранных особенностей поверхностного слоя детали.Аннотация к статье на английском языке: Modern technology is characterized by high reliability and durability, most often connected with a long period of a device’s maintenance with low exploitation costs. In order to achieve operating reliability of modern machines and devices, in many cases unconventional machining technologies are applied that allow for forming special usage qualities of elements. One of the examples may be providing a fault-free exploitation of slide bearing of the shaft neck made of 16MnCr5 steel, for refrigerating unit compressors, where at the final stage of machining the magnetoabrasive polishing technology was used. The paper presents selected research results of the abrasive resistance in elements subject to magnetoabrasive polishing together with the analysis of the constant magnetic field interactions with a ferromagnetic object during such machining. The conducted analysis indicates at a synergic influence of the magnetic field and the machining heat, which allows for obtaining favourable changes to the surface layer (SL) qualities in the object from the tribological point of view. A movement of a steel, hardened object in the magnetic field causes magnetomechanic impact of the fi eld upon ferromagnetic martensite. The magnetic field energy disturbs the primary thermodynamic state of the surface layer zones subject to temperatures from the martensite transformation temperature range. When polishing, the near-surface zones of the surface layer gain high temperature and remain under the influence of high temperature gradient, changing in the layer of several micrometers from the ambient temperature to temperature above Curie point for steel. Experimental research with the X-ray diffraction and the RBS (Rutherford Beam Spectroscopy) method confirmed direct influence of a magnetic field upon the phase composition of hardened steel, and structural research of thin layers of c.a. 100 nm with the application of the Mössbauer spectroscopy indicate at decreasing amount of rudimentary austenite in the surface layer of a steel object after magnetoabrasive polishing.
E-Book Content
Edward WANTUCH Bogusław RAJCHEL Tadeusz BURAKOWSKI Jacek ROŃDA
WPŁYW POLA MAGNETYCZNEGO PODCZAS POLEROWANIA MAGNETOŚCIERNEGO NA WYBRANE CECHY WARSTWY WIERZCHNIEJ PRZEDMIOTU INFLUENCE OF A MAGNETIC FIELD DURING MAGNETOABRASIVE POLISHING UPON THE SELECTED FEATURES OF THE OBJECT’S SURFACE LAYER Wspóczesn technik cechuje wysoka niezawodno i trwao poczona najczciej z wyduonym okresem bezobsugowej pracy urzdze. Dla uzyskania wymaganej niezawodnoci eksploatacyjnej wspóczesnych maszyn i urzdze w wielu przypadkach stosuje si niekonwencjonalne technologie obróbki umoliwiajce ksztatowanie specjalnych waciwoci eksploatacyjnych elementów. Jednym z przykadów moe by zapewnienie bezawaryjnej pracy lizgowych oysk korbowodu, wykonanego ze stali 16MnCr5 do sprarek agregatów chodniczych, dla których w finalnej fazie obróbki czopa wau zastosowano technologi polerowania magnetociernego. Artyku prezentuje wybrane wyniki bada odpornoci na zuycie cierne elementów obrobionych magnetociernie wraz z analiz oddziaywania staego pola magnetycznego z ferromagnetycznym przedmiotem podczas tego rodzaju obróbki. Przeprowadzona analiza wykazuje synergiczny wpyw pola magnetycznego i ciepa obróbki, co umoliwia uzyskanie korzystnych zmian wasnoci war