E-Book Overview
Elseiver. Surface & Coatings Technology xxx (2011) xxx–xxxMicroarc oxidation (MAO) films on AZ31 magnesium alloy were treated by high-intensity pulsed ion beam (HIPIB) irradiation with ion energy of 300 keV at ion current density of 200 A/cm2. A remelted layer of a few micrometers was produced on irradiated MAO films. The corrosion resistance of MAO films was characterized by potentiodynamic electrochemical test in 3.5% NaCl solution. The anodic polarization behavior of MAO samples exhibited a transition from the active anodic dissolution for the original one to the passivation–pitting breakdown for the modified films. The passivation–pitting breakdown voltage of modified films increased with multi-shot irradiation, i.e. from a value of −1420 mV(SCE) at 1 shot to −800 mV(SCE) at 5 shots, and the corresponding passivation current density decreased by two orders of magnitude. The irradiated MAO films have a higher corrosion potential than the original one, reaching a maximal value of −1350 mV(SCE) at 5 shots from the original −1580 mV(SCE). The electrochemical impedance spectrum (EIS) of modified MAO films was measured with varying the immersion time in 3.5% NaCl solution. The Nyquist impedance plots from modified films may show only a capacitive loop at the immersion time of 5 h, and the inductive loop occur at longer immersion time, whereas original films presenting both capacitive and inductive loops at all the immersion time. Bode plots of MAO films before and after irradiation were obviously distinguished in shape at low frequency range, especially at short immersion time. The evolution of Nyquist and Bode plots with immersion time was discussed in association with the processes of electrolyte penetration into the MAO structure and resultant reaction at the film-substrate interface. It is concluded that the improvement in the continuity and compaction of MAO films accounts for the enhanced corrosion resistance of the films irradiated by HIPIB.
E-Book Content
SCT-16684; No of Pages 5 Surface & Coatings Technology xxx (2011) xxx–xxx Contents lists available at ScienceDirect Surface & Coatings Technology j o u r n a l h o m e p a g e : w w w. e l s ev i e r. c o m / l o c a t e / s u r f c o a t Electrochemical properties of microarc oxidation films on a magnesium alloy modified by high-intensity pulsed ion beam X.G. Han, X.P. Zhu, M.K. Lei ⁎ Surface Engineering Laboratory, School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China a r t i c l e i n f o Available online xxxx Keywords: Magnesium alloy Microarc oxidation High-intensity pulsed ion beam Corrosion resistance Electrochemical impedance spectrum a b s t r a c t Microarc oxidation (MAO) films on AZ31 magnesium alloy were treated by high-intensity pulsed ion beam (HIPIB) irradiation with ion energy of 300 keV at ion current density of 200 A/cm2. A remelted layer of a few micrometers was produced on irradiated MAO films. The corrosion resistance of MAO films was characterized by potentiodynamic electrochemical test in 3.5% NaCl solution. The anodic polarization behavior of MAO samples exhibited a transition from the active anodic dissolution for the original one to the passivation– pitting breakdown for the modified films. The passivation–pitting breakdown voltage of modified films increased with multi-shot irradiation, i.e. from a value of − 1420 mV(SCE) at 1 shot to − 800 mV(SCE) at 5 shots, and the corresponding passivation current density decreased by two orders of magnitude. The irradiated MAO films have a higher corrosion potential than the original one, reaching a maximal value of − 1350 mV(SCE) at 5 shots from the original − 1580 mV(SCE). The electrochemical impedance spectrum (EIS) of modified MAO films was measured with varying the immersion time in 3.5% NaCl solution